Er,Yb:ReGa3(BO3)4 (Re = Y, Gd) laser crystals
Another Title
Лазерные кристаллы Er,Yb:ReGa3(BO3)4 (Re = Y, Gd)
Bibliographic entry
Er,Yb:ReGa3(BO3)4 (Re = Y, Gd) laser crystals = Лазерные кристаллы Er,Yb:ReGa3(BO3)4 (Re = Y, Gd) / V. V. Maltsev [и др.] // Приборостроение-2023 : материалы 16-й Международной научно-технической конференции, 15-17 ноября 2023 года, Минск, Республика Беларусь / редкол.: О. К. Гусев (пред.) [и др.]. – Минск : БНТУ, 2023. – С. 322-323.
Abstract
Phase relationships in the ErxYbyY1-x-yGa3(BO3)4-Bi2O3-B2O3-(Y,Er,Yb)2O3–Ga2O3 and ErxYbyGd1-x-yGa3(BO3)4-Bi2O3-B2O3-(Gd,Er,Yb)2O3 – Ga2O3 (x = 0.02, y = 0.11 at.%) system were studied in the temperature range from 1000 to 900 оС. Multicomponent melt Bi2O3-Ga2O3-B2O3-(Y,Gd)2O3 were used as reasonable fluxes for high-temperature solution growth of ErxYbyR1-x-yGa3(BO3)4 (R = Y, Gd) spontaneous crystals. The segregation coefficients of Yb and Er impurities in the obtained crystals are determined. The unit cell parameters for the grown crystals were studied, also showing the micromorphology characteristics of the crystals. The luminescence kinetics were investigated, and the lifetimes of the 4I13/2 energy level of Er3+ ions for Er,Yb:ReGa3(BO3)4 crystals were determined.
Abstract in another language
Изучены фазовые соотношения в системах ErxYbyY1-x-yGa3(BO3)4-Bi2O3-B2O3-(Y,Er,Yb)2O3– Ga2O3 и ErxYbyGd1-x-yGa3(BO3)4-Bi2O3-B2O3-(Gd,Er,Yb)2O3 – Ga2O3 (x = 0,02, y = 0,11 ат.%) в температурном диапазоне 1000-900оС. Выращивание спонтанных кристаллов ErxYbyR1-x-yGa3(BO3)4 (R = Y, Gd) из высокотемпературного раствора-расплава проводилось с использованием сложного растворителя состава Bi2O3-Ga2O3-B2O3-(Y,Gd)2O3. Определены коэффициенты распределения ионов Yb и Er, оценены параметры кристаллической решетки, а также определены морфологические особенности полученных кристаллов. Исследованы кинетики затухания люминесценции и определены времена жизни уровня 4I13/2 ионов Er3+ в кристаллах Er,Yb:ReGa3(BO3)4.