Влияние циркония на прочностные свойства холоднодеформированной арматуры

Thumbnail
DOI
10.21122/1683-6065-2022-1-61-63
Authors
Ельцова, Е. С.
Ходосовская, О. Ю.
Козырева, Ю. И.
Date
2022
Publisher
БНТУ
Another Title
The effect of zirconium on the strength cold-deformed reinforcement properties
Bibliographic entry
Ельцова, Е. С. Влияние циркония на прочностные свойства холоднодеформированной арматуры = The effect of zirconium on the strength cold-deformed reinforcement properties / Е. С. Ельцова, О. Ю. Ходосовская, Ю. И. Козырева // Литье и металлургия. – 2022. – № 1. – С. 61-63.
Abstract
Определена возможность использования циркония в составе стали марки Арх-Zr при изготовлении холоднодеформированной арматуры трехстороннего периодического профиля класса прочности 500 МПа с целью повышения прочностных характеристик готовой арматуры. Приведены данные о результатах испытаний катанки/заготовки диаметром 8,8 мм, которая предназначена для изготовления холоднодеформированной арматуры диаметром 8,0 мм. Выполнен сравнительный анализ физико-механических свойств готовой холоднодеформированной арматуры диаметром 8,0 мм из стали марки Арх-Zr и арматуры трехстороннего периодического профиля, изготовленной из катанки обычного качества. Проведен анализ полученных свойств и оценка холоднодеформированной арматуры на соответствие требованиям стандартов. Выявлено, что добавка в сталь циркония в количестве 0,019 % не оказывает влияния на конечные прочностные характеристики полученной холоднодеформированной арматуры трехстороннего периодического профиля класса прочности 500 МПа. Значения физико-механических параметров полученной холоднодеформированной арматуры аналогичны параметрам холоднодеформированной арматуры, изготовленной из катанки обычного качества без использования легирования.
Abstract in another language
The possibility of using zirconium in the steel composition of the Arx-Zr brand in the cold-deformed reinforcement of a three-sided periodic profile of strength class 500 MPa manufacture in order to increase the finished reinforcement strength characteristics is determined. There is test results information of a wire rod /blank with an 8.8 mm diameter, which is intended for the manufacture of cold-deformed fittings with an 8.0 mm diameter, are presented. A comparative analysis of the physical and mechanical finished cold-deformed fittings properties with an 8.0 mm diameter made of steel grade Arch-Zr and fittings of a three-sided periodic profile made of wire rod of ordinary quality was done. Analyzed the obtained properties and the cold-deformed fittings evaluation for meeting the standards’ requirements. Identified that the addition of zirconium to steel in an amount of 0.019 % does not affect the final strength characteristics of the produced cold-deformed reinforcement of a three-sided periodic profile of strength class 500 MPa. The values of the physical and mechanical parameters of the produced cold-deformed reinforcement are similar to the cold-formed reinforcement parameters made of wire rod of ordinary quality without the use of alloying.
URI
https://rep.bntu.by/handle/data/110146
View/Open
61-63.pdf (263.7Kb)
Collections
  • № 1[25]
Show full item record
CORE Recommender

Belarusian National Technical University | Science Library | About Repository | Размещение в Репозитории | Contact Us
Яндекс.МетрикаIP Geolocation by DB-IP
Science Library | About Repository | Размещение в Репозитории | Contact Us
 

Browse

All of Repository BNTUCommunities & CollectionsAuthorsTitlesBy Issue DatePublisherBy Submit DateTypeThis CollectionAuthorsTitlesBy Issue DatePublisherBy Submit DateType

My Account

LoginRegister

Belarusian National Technical University | Science Library | About Repository | Размещение в Репозитории | Contact Us
Яндекс.МетрикаIP Geolocation by DB-IP
Science Library | About Repository | Размещение в Репозитории | Contact Us